Basic Info.
Product Description
| Physical Property | Unit | Numerical Value |
| Density | g/cm³ | 1.06~1.09 |
| Melting Point | ºC | 207~222 |
| Thermal Deformation Temperature (0.45Mpa) | ºC | 150~180 |
| Tensile Strength | Mpa≥ | 50 |
| Elongation at Break | %≥ | 200 |
| Bending Strength | Mpa≥ | 50 |
| Flexural Modulus | Mpa≥ | 1200 |
| Notch Impact Strength | KJ/m≥ | 6 |
| Molding Shrinkage | % | 1.5~2.0 |
PA610 is a kind of resin material with low density and water absorption, good low temperature performance and easy to dissolve in acid. Mainly used in high-grade toothbrush silk, monofilament, cable coating, machinery manufacturing, oil storage containers, textile machinery parts, in the electronics industry can also be used to make battery cases, instrument guide rails and so on.
Ο With small density and water absorption, low temperature performance
Ο Alkali and dilute inorganic acid, not strong inorganic acid, good weather resistance
Ο Resin material easily soluble in acid
Compared with PA6 and PA66, PA610 resin is more resistant to weak acids, bases and organic solvents, and can dissolve in strong acids, phenols acid. Nylon 610 resin has low water absorption and good low temperature resistance and dimensional stability. Its relative density is small and it has good mechanical strength and toughness. PA610 resin is a self-extinguishing material.
| Building Material Industry | Marble Slab , Abrasive Brush |
| Automotive Industry | Oil Tube |
| Petroleum Industry | High Pressure Tube |
| New Energy Source Industry | Solar Energy, Power Generation |
| Electronics&Electrical Industry | 5G Communication |
| Smart Wearable | Shoe Material, Shoe Arch |
| Aerospace | UAV(Unmanned Aerial Vehicle) |
| Consumption Industry | Wiring Harness |
| Personal Articles Industry | Toothbrush |
Processing and post-treatment of nylon 610 products:
The post-treatment of nylon 610 products is to prevent and eliminate the residual stress in the product or the size change caused by the hygroscopic effect. There are two post-treatment methods: heat treatment and humidity control.
1. In the high boiling point liquid such as mineral oil, glycerin, liquid paraffin, the heat treatment temperature should be 10-20ºC higher than the use temperature, the treatment time varies depending on the wall thickness of the product, the thickness is 10-15 minutes below 3mm, the thickness is 3-6mm, the time is 15-30 minutes, the heat-treated product should pay attention to slow cooling to room temperature. To prevent sudden cooling caused by the stress in the product.
2. Humidification treatment Humidification treatment is mainly carried out on products with large environmental humidity, and there are two methods: a boiling water humidification method, Potassium diacetate aqueous solution humidification method (potassium acetate and water ratio of 1.25:1, boiling point 121ºC), boiling water humidification method is simple, as long as the product is placed in the humidity of 65% environment, so that it can reach the equilibrium moisture absorption, but the time is longer, and potassium acetate aqueous solution humidification method of the treatment temperature of 80-100 potassium acetate aqueous solution humidification method, the treatment time mainly depends on The wall thickness of the product is about 2 hours when the wall thickness is 1.5mm, 8 hours when 3mm, and 16-18 hours when 6mm.